GRADE A32 Unequal Angle Steel Shipbuilding from China

A32 Unequal Angle Steel hasgood toughness properties, higher strength. GRADE A32 are mainly used to contribute hull of ships and the cranes of break bulker and vessels in low temperature oceans, Framework of kinds of construction and engineering. GRADE A32 Unequal Angle Steel is also can be used in some frame part such as construction joist frame, iron tower, derrick frame and so on.

GL A32 chemical composition in angle steel

Grade	C max	Si max	Mn	P max	S max	Als min	Ti max	Cu max	Cr max	Ni max	Mo max
GL-A32	0.18	0.50	0.90-1.60	0.035	0.035	0.015	0.02	0.35	0.20	0.40	0.08

GL-A32 Mechanical Property in shipbuilding angle steel bar, bulb flat bar, L section steel bar

Grade	Rm (MPa)	Re(MPa) min	A% min	Akv/J min
				E.T °C	Thickness (mm)
					≤ 50		>50-70		>70-100
					L	C	L	C	L	C
GL-A32	440-570	315	22	0	31	22	38	26	46	31

GRADE A32 delivery condition:

Grade	Fine grains elements	category	The thickness of steel
			≤ 12	>12.5-20	>20-25	>25-35	>35-50	>50-100
GL-A32	Nb+V or V	Plate/sheet	A(50)	N(50),CR(50),TM(50)				N(50),CR(25),TM(50)
		Profile steel		N(50),CR(50),TM(50),AR*(25)				-
	Al or Al+Ti	Plate/sheet	A(50)		AR*(25)		-
					N(50),CR(50),TM(50)			N(50),CR(25),TM(50)
		Profile steel	A(50)	N(50),CR(50),TM(50),AR*(25)				-

GRADE A32 Unequal Angle Steel Additional Condition

UT(Ultrasonic examination),AR(As Hot Rolled only),TMCP(Thermal Mechanical Control Processing), N(Normalized), Q+T(Quenched and Tempered),Z Direction Test(Z15,Z25,Z35), Charpy V-Notch Impact Test, The Third Party Test(such as SGS Test),Coated or Shot Blasting and Painting.

Other Terms of GRADE A32 Steel:

◆ Packaging Details: Standard export seaworthy packing or as required.
◆ Delivery Time:20-30 days, 7days for stock goods.
◆ Loading Port: Shanghai
◆ Offer Ability:6000MT/Per Month.
◆ MOQ:1 Pcs.

learn more：http://www.section-steel.com/News/GRADE-A32-Unequal-Angle-Steel-Shipbuilding-from-China.html

TEL:0086-21-61182423

Fax :0086-21-61182425

E-mail:service3@katalor.com or liulucy.0212@gmail.com

skype:lisa.liu6282