A387 Grade 12 Class1 steel is a chromium molybdenum alloy steel plates intended primarily for welded boiler and pressure vessels designed of elevated temperature service. Grade 12 Class1 steel has a wide range of uses including industrial boilers and pressure vessels, especially in environments where high temperature levels are common.
A387 Gr.12 CL.1Chemical Composition
Grade
|
The Element Max (%)
| ||||||
C
|
Si
|
Mn
|
P
|
S
|
Cr
|
Mo
| |
A387 Gr.12 Cl.1
|
0.04-0.17
|
0.13-0.45
|
0.35-0.73
|
0.035
|
0.035
|
0.74-1.21
|
0.40-0.65
|
Mechanical Property of A387 Grade 12 Class1 steel
Grade
|
A387 Gr.12 CL.1Mechanical Property
| |||
Thickness
|
Yield
|
Tensile
|
Elongation
| |
A387 Gr.12 Cl.1
|
mm
|
Min Mpa
|
Mpa
|
Min %
|
t≦50
|
230
|
380-550
|
22
| |
50<t≦200
|
-
|
-
|
18
|
Related A387 Grade 12 Class1 grades we could supply:
ASTM A387 boiler and pressure vessel steel plate
| ||
A387Gr12cl1
|
A387Gr12cl2
|
A387Gr11cl1
|
A387Gr11cl2
|
A387Gr22cl2
|
A387Gr22cl1
|
A387Gr22L
|
A387Gr21cl2
|
A387Gr21cl1
|
A387Gr21L
|
A387Gr5cl1
|
A387Gr5cl2
|
A387Gr9cl1
|
A387Gr9cl2
|
A387Gr91cl2
|
A387Gr911cl2
|
A387Gr2cl1
|
A387Gr2cl2
|
UT(Ultrasonic examination),AR(As Hot Rolled only),TMCP(Thermal Mechanical Control Processing), N(Normalized), Q+T(Quenched and Tempered),Z Direction Test(Z15,Z25,Z35),Charpy V-Notch Impact Test, The Third Party Test(such as SGS Test),Coated or Shot Blasting and Painting.
Other Terms of A387 Grade 12 Class1 steel
◆Packaging Details: Standard export seaworthy packing or as required.
◆Delivery Time: 20-30 days, 5-7 days for stock goods.
◆Loading Port: Shanghai
◆Offer Ability: 6 000MT/Per Month.
◆Delivery Time: 20-30 days, 5-7 days for stock goods.
◆Loading Port: Shanghai
◆Offer Ability: 6 000MT/Per Month.
learn more:http://construction-steel.com/News/Different-Grades-of-A387-Grade-12-Class1-Boiler-Steel-Plate.html
TEL:0086-21-61182423
Fax :0086-21-61182425
E-mail:service3@katalor.com or liulucy.0212@gmail.com
Fax :0086-21-61182425
E-mail:service3@katalor.com or liulucy.0212@gmail.com
skype:lisa.liu6282
没有评论:
发表评论