The chemical composition of grade 202 stainless steel
Element |
Content (%)
|
Iron, Fe |
68
|
Chromium, Cr |
17- 19
|
Manganese, Mn |
7.50-10
|
Nickel, Ni |
4-6
|
Silicon, Si |
≤ 1
|
Nitrogen, N |
≤ 0.25
|
Carbon, C |
≤ 0.15
|
Phosphorous, P |
≤ 0.060
|
Sulfur, S |
≤ 0.030
|
Properties |
Metric
|
Imperial
|
Tensile strength |
515 MPa
|
74694 psi
|
Yield strength |
275 MPa
|
39900 psi
|
Elastic modulus |
207 GPa
|
30000 ksi
|
Poisson's ratio |
0.27-0.30
|
0.27-0.30
|
Elongation at break |
40%
|
40%
|
1, Corrosion resistance
2, Durable
3, Dimensional accuracy.
4, Chemical resistance.
5, High Strength
6, Fine Finish
learn more:http://www.ice-steels.com/News/ASTM-A240-Grade-202S20200-Stainless-Steel-Manufacturing-Process.html
TEL:0086-21-61182423
Fax :0086-21-61182425
E-mail:service3@katalor.com or liulucy.0212@gmail.com
Fax :0086-21-61182425
E-mail:service3@katalor.com or liulucy.0212@gmail.com
skype:lisa.liu6282
没有评论:
发表评论