ASTM A240 2304 Chemical Composition
Grade
|
The Element Max (%)
|
||||||
C
|
Mn
|
P
|
S
|
Si
|
Cr
|
Ni
|
|
ASTM A240 2304
|
0.03
|
2.5
|
0.040
|
0.030
|
1.0 |
21.5-24.5
|
3.0-5.5 |
Mo
|
N
|
Cu
|
Cb |
Ti |
|
|
|
0.05-0.60
|
0.05-0.20 |
- |
- |
- |
|
|
Grade
|
ASTM A240 2304 Mechanical Property
|
||||
Yield
|
Tensile
|
Elongation
|
Hardness, max
|
||
ASTM A240 2304
|
Min Mpa
|
Mpa
|
Min %
|
Brinell
|
Rockwell B
|
400
|
600
|
25%
|
290
|
|
2304(S32304) Stainless Steel is mainly used in Water heaters, Heat exchangers, Pressure vessels, Feed water tubes, Heat exchangers, Flue-gas, cleaning, Seawater systems, Desalination plants, Parts for structural design, Rotors, impellers and shafts, Firewalls and blast walls on offshore platforms, Cargo tanks and pipe systems in chemical tankers, Piping and instrumentation tubing for general service.
ASTM 2304(S32304) Stainless Steel Manufacturing Process
Duplex 2304 Welding can be performed using most of the traditional methods such as gas–tungsten arc welding (GTAW), submerged arc welding (SAW), and gas–metal arc welding (GMAW).
2304 STAINLESS steel Hot working can be done after heating the material to 954-1093°C (1750-2000°F), which is followed rapid cooling. Annealing after working is recommended.
learn more:http://www.ice-steels.com/News/ASTM-2304S32304-Stainless-Steel-ASTM-Equivalent.html
TEL:0086-21-61182423
Fax :0086-21-61182425
E-mail:service3@katalor.com or liulucy.0212@gmail.com
Fax :0086-21-61182425
E-mail:service3@katalor.com or liulucy.0212@gmail.com
skype:lisa.liu6282
没有评论:
发表评论