ASTM A240 329 Chemical Composition
Grade
|
The Element Max (%)
|
||||||
C
|
Mn
|
P
|
S
|
Si
|
Cr
|
Ni
|
|
ASTM A240 329
|
0.08
|
1.0
|
0.04
|
0.030
|
0.75 |
23-28
|
2.0-5.0 |
Mo
|
N
|
Cu
|
Cb |
Ti |
W |
|
|
1.0-2.0 |
|
|
|
|
|
|
Grade
|
ASTM A240 329 Mechanical Property
|
||||
|
|||||
Yield
|
Tensile
|
Elongation
|
Hardness, max
|
||
ASTM A240 329
|
Min Mpa
|
Mpa
|
Min %
|
Brinell
|
Rockwell B
|
485
|
620
|
15%
|
269
|
|
One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, S32900 is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.
SS 329 Machinability
Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition
S32900 Welding
Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding.
1.4460 Forging
Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.
learn more:http://www.ice-steels.com/News/Duplex-Stainless-Steel-SS-329-S32900-14460-Maching-Performance.html
TEL:0086-21-61182423
Fax :0086-21-61182425
E-mail:service3@katalor.com or liulucy.0212@gmail.com
Fax :0086-21-61182425
E-mail:service3@katalor.com or liulucy.0212@gmail.com
skype:lisa.liu6282
没有评论:
发表评论