How does ASTM A240 S30100 Stainless Steel Compare to Other Iron Alloys

S30100 is an austenitic stainless steel with a nominal composition of 17 percent chromium and 7 percent nickel. ASTM A240 S30100 stainless steel is available as cold rolled strip, sheets, and plates from ATI.

ASTM A240 301 Chemical Composition

Grade
The Element Max (%)
C
Mn
P
S
Si
Cr
Ni
ASTM A240 301
0.15
2.0
0.045
0.030
1.0
16.0-18.0
6.0-8.0
Mo
N
Cu
 
 
 
 
 
0.10
 
 
 
 
 
ASTM A240 301 Mechanical Property
Grade
 
Yield
Tensile
Elongation
Hardness, max
ASTM A240 301
Min Mpa
Mpa
Min  %
Brinell
Rockwell B
205
515
40%
217
95
Austenitic Stainless Steel
Carbon Steel
Cast Iron
Duplex (Austenitic-Ferritic) Stainless Steel
Low-Alloy Steel
Low-Expansion Iron Alloy
Otherwise Unclassified Iron Alloy
Precipitation-Hardening (PH) Stainless Steel
ASTM A240 S30100 stainless  steel is resistant to a variety of corrosive media. However, the corrosion properties are not as good as the 18-8 chromium-nickel steels. Its susceptibility to carbide precipitation during welding restricts its use in many applications in favor of ATI 304 or ATI 304L alloys.
Oxidation Resistance ASTM A240 301
ASTM A240 S30100 stainless  steel possesses good resistance to oxidation at temperatures up to 1550°F (840°C). At 1600°F (871°C), ATI 301™ alloy exhibits an oxidation weight gain of 10mg/cm2 in 1,000 hours. Therefore, this stainless steel is not suggested for use at 1600°F or above.
Shanghai Katalor Enterprises Co., Ltd is a big complex combined steel stockist whose business related with trade, processing, storage and transportation. we are specialized in supplying ASTM A240 S30100 stainless steel.  We have the good quality and advanced equipment, our products meet the state standard, and also available for customers' requirement. If you have any need of S30100,  please do not hesitate to contact us by email info@katalor.com, we can do our best to help you!
learn more:http://construction-steel.com/News/How-does-ASTM-A240-S30100-Stainless-Steel-Compare-to-Other-Iron-Alloys.html