1.0204 steel Heatment Analysis

1.0204 steel is one of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, 1.0204 steel is capable of high properties with a single precipitation or aging treatment. 1.0204 stee is characterized by good corrosion resistance, high harness, toughness and strength.

Chemical composition % of the ladle analysis of grade DIN 1.0204 and Standards
Element
Weight%
C
0.10 (max)
Mn
0.30-0.50
P
0.04 (max)
S
0.05 (max)

1.0204 steel Mechanical Properties
 
 
Properties
Conditions
T(°C)
Treatment
Density(×1000 kg/m3)
7.871
25

Poisson's Ratio
0.27-0.30
25

Elastic Modulus(GPa)
190
25

Tensile Strength(Mpa)
34025
cold drawn (round bar (19-32 mm))more
Yield Strength(Mpa)
285
Elongation(%)
20
Reduction in Area(%)
45
Hardness(HB)
95
25
cold drawn (round bar (19-32 mm))more
 
 
1.0204 steel can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.
1.0204 Steel Heat Treatment
CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool.
Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding.
As a very long history company, Shanghai Katalor Enterpriseshad enough experience about the quality, price for these goods in China Market. we are a professional 1.0204 steel stockist and supplier. We can supply different product type and grades of1.0204 steel. If you want to get the price, please do not hesitate tocontact us.
Company Name: Shanghai Katalor Enterprises
Address:Room 301,Unit 6,lane 2500,xiupu Road, Kang qiao Industrial Area, Pu dong New District, Shanghai
TEL:0086-21-61182423
Fax :0086-21-61182425

E-mail:info@katalor.com
Phone:0086-18317160019

没有评论:

发表评论