904 L Stainless Steel Composition Ranges

UNS NO8904, commonly known as 904L, is a low carbon high alloy austenitic stainless steel .904L is an austenitic stainless steel designed for moderate to high corrosion resistance. Its low carbon content improves cleanliness and weld strength. Utility scrubber assemblies, acid and fertilizer production equipment.

Composition ranges of grade 904L stainless steels

Grade
C
Mn
Si
P
S
Cr
Mo
Ni
Cu
904L
min.
max.
-
0.02
-
2
-
1
-
0.045
-
0.035
19
23
4
5
23
28
1
2
Mechanical properties of grade 904L stainless steels

Grade
Tensile Strength (MPa) min
Yield Strength 0.2% Proof (MPa) min
Elongation (% in 50mm) min
Hardness
Rockwell B (HR B)
Brinell (HB)
904L
490
220
36
70-90 typical
150
Pulp and paper processing industries
Wiring in electrostatic precipitators
Oil refinery components
Seawater cooling devices
Gas scrubbing plant
DESIGN FEATURES of grade 904L stainless steels
1,Good resistance to pitting and crevice corrosion.
2,Very good resistance to stress corrosion cracking.
3, Maximum service temperatures of 450 deg.C. (824 deg.F).
Heat Resistance
Grade 904L stainless steels offer good oxidation resistance. However, the structural stability of this grade collapses at high temperatures.
Grade 904L stainless steels can be solution heat-treated at 1090 to 1175°C, following by rapid cooling.
Welding
Welding of grade 904L stainless steels can be performed using all conventional methods. This grade does not require pre-heat and post-weld heat treatments.
We have our own processing factory and the pre- treatment factory, pre-treatment for stainless steel. And we can also make the customers enjoy our other pre-treatment services, like cutting, welding, drilling holes, galvanizing by the lowest cost price. We are a professional UNS NO8904 steel  exporter and Stockist in china. Any need in904L , please feel free to contact us by email or calling to us by email imfo@Katalor.com.
learn more:http://construction-steel.com/News/904-L-Stainless-Steel-Composition-Ranges.html