CCS EH36 Shipbuilding Steel Chemical Composition and Mechanical Property

EH36 steel grade is lower than FH36 inyield and tensile strength. Shipbuilding steel plate CCS Grade EH36 is mainly used to make ship cranes owning to its alloy elements and high strength property. CCS Grade EH36 shipbuilding steel plate is also used in building decks of ships, vessels and boats, other normal repairing works in shipyards.

CCS Grade EH36 Chemical Composition and Mechanical Property
GradeChemical Composition(%)
CMn≥SiPS
CCS EH360.180.90-1.600.10-0.500.0350.035
GradeMechanical Property
Tensile Strength(MPa)Yield Strength(MPa)% Elongation in 2 in.(50mm) minImpacting Test Temperature(°C)
CCS EH36440-59031522-40










CCS Steel Plate Grade
General StrengthCCS/ACCS/BCCS/DCCS/E
High StrengthCCS/A32CCS/D32CCS/E32CCS/F32
CCS/A36CCS/D36CCS/E36CCS/F36
CCS/A40CCS/D40CCS/E40CCS/F40
Extra StrengthCCS/A420CCS/D420CCS/E420CCS/F420
CCS/A460CCS/D460CCS/E460CCS/F460
CCS/A500CCS/D500CCS/E500CCS/F500
CCS/A550CCS/D550CCS/E550CCS/F550
CCS/A620CCS/D620CCS/E620CCS/F620
CCS/A690CCS/D690CCS/E690CCS/F690
Steel Grade: Grade EH36
Steel Standard: China Classification Society (CCS)
Thickness: 2mm-350 mm
Width: 1200mm-4200 mm
Length: 3000 mm-12000 mm
Meanwhile, the size can be customized.
Shanghai Katalor Enterprises is focus on steel export. We main provide steel plates, steel coils, steels, pipes, stainless steel and alloy steel bars. We had established long term strategic cooperative relationships with Chinese mostly steel mills, such as Bao Steel, Shou gang Group, Wuhan Iron and Steel, SINO Steel.
we are a professional CCS Grade EH36 stockist and supplier. We can supply different product type and grades of CCS Grade. If you want to get the CCS Grade EH36 shipbuilding steel plate price, please do not hesitate tocontact us.
TEL:0086-21-61182423
Fax :0086-21-61182425
E-mail:info@katalor.com
Phone:0086-18317160019
learn more:http://www.heavy-steels.com/news/CCS-EH36-Shipbuilding-Steel-Chemical-Composition-and-Mechanical-Property.html

没有评论:

发表评论