ASTM A283 Grade C Steel Plate is a kind of common carbon structure steel. The tensile of ASTM A283 GR.C is low or mid-low.A283 steel grade covers four grades in A283 Grade a, A283 Grade B, A283 Grade C, and A283 Grade D of carbon steel plates of structural quality for general application.

ASTM A283 Steel Plate Chemical Properties

Grade A
Grade B
Grade C
Grade D
Carbon, max
0.14
0.17
0.24
0.27
Manganese, max
0.90
0.90
0.90
0.90
Phosphorus, max
0.035
0.035
0.035
0.035
Sulphur, max
0.04
0.04
0.04
0.04
Silicon
Plates 1 1/2 in and under, max
Plates over 1 1/2 in

0.40
0.15-0.40

0.40
0.15-0.40

0.40
0.15-0.40

0.40
0.15-0.40
Copper min % when copper steel is specified
0.20
0.20
0.20
0.20
ASTM A283 Steel Mechanical Properties

Grade A
Grade B
Grade C
Grade D
Tensile Strength:
45,000 -60,000 psi
[310 - 415 MPa]
50,000 -65,000 psi
[345 - 450 MPa]
55,000 75,000 psi
[380 - 515 MPa]
60,000 -80,000 psi
[415 - 550 MPa]
Min. Yield Point:
24,000psi
[165 MPa]
27,000psi
[185 MPa]
30,000psi
[205 MPa]
33,000psi
[230 MPa]
Elongation in 8":
27% min
25% min
22% min
20% min
Elongation in 2":
38% min
28% min
25% min
23% min
ASTM A283Grade C Steel Plate Specification
Material:ASTM A283 GR.C
Standard:ASTM
Thickness: 6-80mm,
Width: 1500-3000mm,
Length: 6000-12000mm
We can supply any size based on customer's requirements.
As a very long history company, Shanghai Katalor Enterpriseshad enough experience about the quality, price for these goods in China Market. we are a professional ASTM A283Grade C stockist and supplier. We can supply different product type and grades of ASTM A283 Steel Plate. If you want to get the price, please do not hesitate tocontact us.

Company Name: Shanghai Katalor Enterprises
Address:Room 301,Unit 6,lane 2500,xiupu Road, Kang qiao Industrial Area, Pu dong New District, Shanghai
TEL:0086-21-61182423
Fax :0086-21-61182425

E-mail:info@katalor.com or liulucy.0212@gmail.com
Phone:0086-18317160019
learn more:http://www.ice-steels.com/News/ASTM-A283Grade-C-Steel-Plate-Unique-Use.html

没有评论:

发表评论