The chemical composition of grade 309 stainless steel.
Element |
Content (%)
|
Iron, Fe |
60
|
Chromium, Cr |
23
|
Nickel, Ni |
14
|
Manganese, Mn |
2
|
Silicon, Si |
1
|
Carbon, C |
0.20
|
Phosphorous, P |
0.045
|
Sulfur, S |
0.030
|
Properties |
Metric
|
Imperial
|
Tensile strength |
620 MPa
|
89900 psi
|
Yield strength (@ strain 0.200%) |
310 MPa
|
45000 psi
|
Izod impact |
120 - 165 J
|
88.5 - 122 ft-lb
|
Shear modulus (typical for steel) |
77 GPa
|
11200 ksi
|
Elastic modulus |
200 GPa
|
29008 ksi
|
Poisson's ratio |
0.27-0.30
|
0.27-0.30
|
Elongation at break (in 50 mm) |
45%
|
45%
|
Hardness, Brinell |
147
|
147
|
Hardness, Rockwell B |
85
|
85
|
Hardness, Vickers (converted from Rockwell B hardness) |
169
|
169
|
1, Heating elements
2, Aircraft and jet engine parts
3, Heat exchangers
4, Carburizing annealing products
5, Sulfite liquor handling equipment
6, Kiln liners
7, Boiler baffles
8, Refinery and chemical processing equipment
9, Auto exhaust parts
309s stainless steel specification:
Thickness From 0.3mm to 150mm Width 1000mm, 1219mm, 1250mm, 1500mm, 1800mm, 2200mm or as your requirement Length 2000mm, 2438mm, 2500mm, 6000mm, 6096mm or as your requirement
learn more:http://www.ice-steels.com/News/Hot-Sale-ASTM-A240-309s-Stainless-Steel-Wholesale-Price-Before-Chinese-Holiday.html
TEL:0086-21-61182423
Fax :0086-21-61182425
E-mail:service3@katalor.com or liulucy.0212@gmail.com
Fax :0086-21-61182425
E-mail:service3@katalor.com or liulucy.0212@gmail.com
skype:lisa.liu6282
没有评论:
发表评论