Chemical composition % of grade 310 and 310S stainless steel
Chemical Composition |
310
|
310S
|
Carbon
|
0.25 max
|
0.08 max
|
Manganese
|
2.00 max
|
2.00 max
|
Silicon
|
1.50 max
|
1.50 max
|
Phosphorus
|
0.045 max
|
0.045 max
|
Sulphur
|
0.030 max
|
0.030 max
|
Chromium
|
24.00 - 26.00
|
24.00 - 26.00
|
Nickel
|
19.00 - 22.00
|
19.00 - 22.00
|
Mechanical Properties |
310/ 310S
|
Grade 0.2 % Proof Stress MPa (min)
|
205
|
Tensile Strength MPa (min)
|
520
|
Elongation % (min)
|
40
|
Hardness (HV) (max)
|
225
|
310S Stainless Steel chips are stringy and it will work harden rapidly. It is necessary to keep the tool cutting at all times and use chip breakers.