Composition ranges for 316L stainless steels
Grade |
|
C
|
Mn
|
Si
|
P
|
S
|
Cr
|
Mo
|
Ni
|
N
|
316L
|
Min
|
-
|
-
|
-
|
-
|
-
|
16.0
|
2.00
|
10.0
|
-
|
Max
|
0.03
|
2.0
|
0.75
|
0.045
|
0.03
|
18.0
|
3.00
|
14.0
|
0.10
|
Grade |
Tensile Str
(MPa) min |
Yield Str
0.2% Proof (MPa) min |
Elong
(% in 50mm) min |
Hardness
|
|
Rockwell B (HR B) max
|
Brinell (HB) max
|
||||
316L
|
485
|
170
|
40
|
95
|
217
|
Grade |
Why it might be chosen instead of 316?
|
317L
|
Higher resistance to chlorides than 316L, but with similar resistance to stress corrosion cracking.
|
1, Chemical processing, equipment
2, Laboratory benches and equipment
3, Rubber, plastics, pulp paper machinery
4, Pollution control equipment
5, Boat fittings, value and pump trim
learn more:http://www.ice-steels.com/News/ASTM-A240-Grade-316L-S31603-Stainless-Steel-Hot-and-Cold-Working.html
TEL:0086-21-61182423
Fax :0086-21-61182425
E-mail:service3@katalor.com or liulucy.0212@gmail.com
Fax :0086-21-61182425
E-mail:service3@katalor.com or liulucy.0212@gmail.com
skype:lisa.liu6282
没有评论:
发表评论