S355JR I Beam is a low carbon, high tensile strength structural steel which can be readily welded to other weld able steel, EN10025-2 S355JR is produced by fully killed steel process and supplied in normalized or controlled rolling condition.
Chemicalcomposition % of the ladle analysis of grade S355JR
| Nominalthickness=<30(mm)CEVmax=0.45 | |||||||
| C | Si | Mn | P | S | N | Cu | CEV |
| max0.24 | max0.55 | max1.6 | max0.04 | max0.04 | max 0.012 | max0.55 | max0.47 |
Mechanical properties of grade S355JR
| Nominalthickness(mm) | to16 | 16-40 | 40-63 | 63-80 | 80-100 | 100-125 |
| ReH-Minimumyieldstrength(MPa) | 355 | 345 | 335 | 325 | 315 | 295 |
| Temperature | -20 | 0 | 20 |
| Notchimpacttest.Min.absorbedenergy | 27 | 27 | 27 |
S355JR I Beam Additional Condition
UT(Ultrasonic examination),AR(As Hot Rolled only),TMCP(Thermal Mechanical Control Processing), N(Normalized), Q+T(Quenched and Tempered),Z Direction Test(Z15,Z25,Z35),Charpy V-Notch Impact Test, The Third Party Test(such as SGS Test),Coated or Shot Blasting and Painting.
◆Packaging Details: Standard export seaworthy packing or as required.
◆Delivery Time: 20-30 days, 5-7 days for stock goods.
◆Loading Port: Shanghai
◆Offer Ability: 6 000MT/Per Month.
◆Delivery Time: 20-30 days, 5-7 days for stock goods.
◆Loading Port: Shanghai
◆Offer Ability: 6 000MT/Per Month.
skype: lisa.liu6282
没有评论:
发表评论