EN10025 S355 J0 H Section Steel Chemical Composition Analysis
Grade
|
% by max
|
|||||||
Name
|
Number
|
C
|
Si
|
Mn
|
P
|
S
|
N
|
Cu
|
S355J0
|
1.0553
|
0.23
|
0.60
|
1.70
|
0.040
|
0.040
|
0.014
|
0.60
|
Grade
|
Yield strength
MPa |
Tensile strength
MPa |
Elongation
% |
Minimum impact
J Thickness≤ 150 mm |
Test temperature
℃ |
||
Thickness mm
|
Thickness mm
|
Thickness mm
|
|||||
Name
|
Number
|
≤16
|
>16
≤40 |
≥3
≤40 |
≥3
≤40 |
||
S355J0
|
1.0553
|
355
|
345
|
470-630
|
22
|
27
|
0
|
1,Better Bending ability, about 5% to 10% over than I beam.
2,Two surfaces of Flanges parallel to each other so that it is easy to connecting, processing, install.
3,Compared with the welding I beam, low-cost, high-precision, low residual stress, and do not need the expensive welding materials and weld inspection, it will saving about 30% Steel production cost
4,Same cross-section under load. Hot-rolled steel H Beam is lighter than conventional steel about 15% -20%.
We are a trusted and reliable brand for our high quality and good manufacturing of EN 10025-2 S355 J0 H Section .Our company has been a manufacturer and exporter of EN 10025-2 S355 J0 H Section for decades, and has been sold all over the world with favorable price. As a responsible enterprise, we always stick to be your satisfying partner.
Company Name: Shanghai Katalor Enterprises
Address:Room 301,Unit 6,lane 2500,xiupu Road, Kang qiao Industrial Area, Pu dong New District, Shanghai
TEL:0086-21-61182423
Fax:0086-21-61182425
E-mail:info@katalor.com
Phone:0086-18317160019
learn more:http://www.ice-steels.com/News/EN-100252-S355-J0-H-Section-Special-Use.html
没有评论:
发表评论